| 双层阳光板 | 厚度Thickness | 长度Length | 宽度Width | 重量Weight | 半径Radius | 透光率 Light transmission %(±3%) | |||||
| mm | mm | mm | kg | mm | 透明 Bromsparent |
茶色 Bronze |
乳白 Ivory |
宝兰 Sapphire blue |
湖蓝色 Lake Blue |
草绿色 Light-green |
|
| 4 | 6000 | 2100 | 0.9 | 700 | 80 | 58 | 57 | 45 | 55 | 45 | |
| 6 | 6000 | 2100 | 1.3 | 1050 | 79 | 50 | 56 | 36 | 50 | 42 | |
| 8 | 6000 | 2100 | 1.5 | 1400 | 78 | 44 | 52 | 30 | 47 | 40 | |
| 10 | 6000 | 2100 | 1.7 | 1750 | 78 | 40 | 44 | 28 | 42 | 35 | |
| 12 | 6000 | 2100 | 2.2 | 2100 | 78 | 38 | 42 | 25 | 40 | 34 | |
| 性能 （characteristics） | 单 位 (Unit) | 中空板指标值(Data) |
| 冲击强度（Impact strength) | J/m | 850 |
| 透光率（Light Transmission) | % | 25~82 |
| 比重 （Specific Gravity) | g/cm | 1.2 |
| 热膨胀系数（Coefficentof Thermal Expansion) | mm/m℃ | 0.065 |
| 可耐温度（Service Temperature) | ℃ | -40℃+120℃ |
| 抗拉强度（Tensile Strength) | N/mm | >60 |
| 弯曲强度（Flexural Strength) | N/mm | 100 |
| 弹性模量（Modulus of Elasticity) | Mpa | 2400 |
| 断裂拉伸应力（Elongation at Break) | Mpa | >65 |
| 断裂拉伸率（Elongation at Break) | % | >100 |
| 热变形温度（Heat Deflection Temperature) | ℃ | 1.20 |
| 隔音效果（Effect of Soundproof) | 10mm中空板减少20分贝 |
透光性：高透光性，视颜色不同，透光率可达25%-82%。
抗冲击性：：中空板的冲击强度是玻璃的80倍，在安装及使用过程中不易损坏。
防紫外线：：PC板采用三层共挤方式生产，表面覆盖一层高浓度紫外线吸收剂，并可以保持长久耐候。板材在-40℃~120℃可保持良好物理特性。
隔音：：中空结构和聚碳酸酯有良好的隔音特性，能有效地降低噪音。
重量轻：：中空板的重量是同厚度玻璃重量的1/12，节省建筑结构成本和人力。
加工性好：：可用一般木工工具切割，无须专门配备专用工具，弯曲半径为板厚的175倍，可冷弯安装适合各种造型。
节能：：传热系数低（K值），因此具有良好的隔热性能。与相同厚度的玻璃相比节能潜力高达1.7倍。
耐候性：：加速老化测试4000小时后，▲YI为2， ▲LT仅降低0.6%，证明在使用10年后仍然保持高透光率，低黄变度。
耐燃性：：Sunlight多层板材符合GB8624-2006标准，为“难燃”（B-s2,vd0）